Stulz Sickles Steel
Characteristics
Resists all Impact and Abrasion
Work Hardens Rapidly up to 550 Brinell Due to High Carbon Content
Remains Ductile Throughout, Never Brittle
Work Hardened Surface Becomes Almost Friction- Less Which Allows the Materials to Slide Easily
Has Non-Magnetic Property
Can Be Cut By Oxy-Acetylen E Torch, Plasma, Water Jet, Or Laser
Hadfield Grade
Fully Heat Treated
Fully Austenitic
ASTM A128
Weld with Stulz Manganese-XL or Stulz 1616
Manganal is Used Here for Maintenance and Repair Within the Foundry and Shot Blast Industries . . . Barrel Head Liners, Floor Liners, Wheel Housings, Chains, Cab. Wall Liners , Table Liners, Flights, Hooks, Hanging Liners, Table Rings, Blasting Trees, Shafts, Rotary Screen Separators, Floor Gratings . . . and any other places where heavy impact, abrasion or metal-to-metal wear is a problem.
Fabricated Parts to Specification Welded, Punched, Drilled and Formed Fabrications will be Quoted on Submission of Sketch or Blueprint Specifications.
Flats Wear Resistant High Manganese High Carbon Steel
Rounds Wear Resistant High Manganese High Carbon Steel
Squares Wear Resistant High Manganese High Carbon Steel
Plates Wear Resistant High Manganese High Carbon Steel
Angles Wear Resistant High Manganese High Carbon Steel
Pins & Bushings Wear Resistant High Manganese High Carbon Steel
Shot-Blast Grating Wear Resistant High Manganese High Carbon Steel
Wire Screen - Custom Produced,Various Wire Diameters,Standard Square Openings,Standard Weaves
Wear Bars - Wear Bars on Bottom of Excavator Bucket
Grizzly Bars - can be Flame Cut/Plasma Cut.
Grizzly Bars after two years of service. Prior to switching to manganal, the customer was building up bars yearly.
Manganal side plates show little wear after two years
Bucket Liners